Volume 2, pages 62-63, 1917

     MIRABILITE FROM THE ISLE ROYALE COPPER MINE, HOUGHTON, MICHIGAN.

     ALBERT B. PECK University of Michigan

     During the fall of 1916 the Mineralogical Laboratory of the University of Michigan received from Professor A. C. Lane of Tufts College a sample of a fibrous mineral which upon investigation proved to be the rather uncommon mineral mirabilite. The material was obtained by Dr. Lane and Mr. A. H. Wohlrab, assistant to the superintendent of the Isle Royale Copper Company, from the 26th level, Shaft No. 2 of the Isle Royale Mine. Subsequently Mr. Wohlrab furnished another sample but this was from the "old workings of the No. 1 Shaft." I am greatly indebted to these gentlemen for so kindly placing this material at my disposal. The material consists of a mass of colorless interlocking fibers, clear and transparent for the most part, and frequently very much twisted and bent. A small amount of clayey matter is present as an admixture. Upon exposure to the air, the fibers soon crumble to a white powder.

     A preliminary examination before the blowpipe showed the presence of much sodium, sulfur and water, with traces of potassium, chlorine, calcium and aluminium, the last two being contained in the clayey material referred to above. Quantitative analysis yielded the result of table 1.

     The mineral was first dried in an air bath at 130°C. until it showed a constant weight. This served to drive off all water. The fact that the water content, and consequently the molecular ratio, is somewhat lower than the theoretical value is easily accounted for when it is considered that the original material taken for analysis had already been partially dehydrated by exposure to air. Upon solution in water an insoluble residue of earthy material was obtained. Sulfur was determined by precipitation with BaCl, and weighing as BaSO4. Na2O was determined by the difference in weight of the combined chlorides of sodium and potassium after the latter had been found as the chloro-platinate (K2PtCl2). The analysis and the ratios calculated therefrom establish conclusively that the substance under consideration is the mineral mirabilite (Na2SO4.10H2O).

     TABLE 1

  1 2 3 4   5
Na2O 17.84 19.02 19.25 0.3067 0.3148 1.000
K2O 0.72 0.77   0.0081
CaO trace          
SO3 23.81 25.37 24.86 0.3168   1.006
Cl trace          
H2O 51.4 54.84 55.89 3.0466   9.677
Insoluble 5.69          
   99.50 100.00 100.00      

     1. Results of analysis. 2. Same, after removing insoluble matter and recalculating to 100%. 3. Theory for Na2SO4.10H2O. 4 and 5. Ratios shown by 2.

     This is further confirmed by the determination of the optical constants. By using the immersion method a mean index of refraction of 1.437 ±0.005 was obtained. This compares very favorably with the value given by Miller1 of approximately 1.44 for β. The double refraction is very weak, low gray interference colors predominate and only the thicker sections show distinct colors. The optical character of the mineral is negative as is also its principal zone. The apparent optic angle (2E) is large.

     It is thought that this is the first time mirabilite has been reported as occurring in Michigan. Except for its formation in large quantities in the salt lakes of the west, it is a mineral met with rather infrequently because of its great solubility and unstable character.

NOTE

       1 Trans. Cambridge Phil. Soc., 7, 215, 1842.